Modified Aliphatic Amines are room temperature reacting
curing agents derived from aliphatic amines. The basic
aliphatic amines are modified to reduce their vapor-pressure
and thereby reduce their corrosiveness. The modification
is also done to optimize the hardness, reactivity,
handling time of system and also to improve the carbonation
resistance. |
| Grade |
TH7201 |
| Colour1 |
3 |
| Viscosity2 |
20 - 60 |
| Amine value3 |
475 - 520 |
| Specific gravity4 |
1.06 |
| Equivalent
weight per active-H |
60 |
| Recommended
phr5 |
33 |
| Gel time6 |
18 - 30 |
| Thin film
set time7 |
2 - 3 |
| Tg8 |
74 - 78 |
| General Comments |
Exhibits outstanding
resistance to strong oxidizing acids, many bases,
chlorinated hydrocarbons and methanol gasoline mixtures.
Contributes to high
chemical resistance when it is cured with EPOTEC YD
128 or EPOTEC YDPN 661 multifunctional epoxy resins. |
| Downloads |
TDS
(.pdf 31kb) |
 |
| Grade |
TH7202 |
| Color1 |
3 |
| Viscosity2 |
80 - 130 |
| Amine value3 |
1,050 - 1,080 |
| Specific gravity4 |
1.04 |
| Equivalent
weight per active-H |
31 |
| Recommended
phr5 |
15 |
| Gel time6 |
10 - 16 |
| Thin film
set t ime7 |
2 - 3 |
| Tg8 |
min 50 |
| General Comments |
Has low viscosity
and cures rapidly at
room temperature. Provides high strength and has good
resistance to chemicals. Used in grouts, as adhesive
for fixing road reflectors, gel coats and as an accelerator
for other hardeners. |
| Downloads |
TDS
(.pdf 32kb) |
|
| Grade |
TH7203 |
| Color1 |
3 |
| Viscosity2 |
250 - 400 |
| Amine value3 |
360 - 380 |
| Specific gravity4 |
1.1 |
| Equivalent
weight per active-H |
88 |
| Recommended
phr5 |
46 |
| Gel time6 |
25 - 30 |
| Thin film
set t ime7 |
2 - 3 |
| Tg8 |
50 - 6,010 |
| General Comments |
Excellent
chemical resistance, capable to cure at 10oC.
Can be used for chemically resistant floorings and
as an accelerator for other amine curing agents. |
| Downloads |
TDS
(.pdf 28kb) |
|
| Grade |
TH7207 |
| Color1 |
3 |
| Viscosity2 |
150 - 350 |
| Amine value3 |
615 - 675 |
| Specific gravity4 |
0.97 |
| Equivalent
weight per active-H |
95 |
| Recommended
phr5 |
50 |
| Gel time6 |
8 -12 |
| Thin film
set t ime7 |
1- 2 |
| Tg8 |
50 - 7,011 |
| General Comments |
Faster cure
even in presence of high humidity. Can be used for
solvent free coatings, floorings and as an accelerator
for other amine curing agents. |
| Downloads |
TDS
(.pdf 27kb) |
|
| Grade |
TH7210 |
| Color1 |
4 |
| Viscosity2 |
3,000 - 4,500 |
| Amine value3 |
770 - 820 |
| Specific gravity4 |
1.07 |
| Equivalent
weight per active-H |
38 |
| Recommended
phr5 |
20 |
| Gel time6 |
12 - 16 |
| Thin film
set t ime7 |
3 - 4 |
| Tg8 |
55 - 10,512 |
| General Comments |
Provides surfaces
with very good hydrocarbon resistance. Used in high
solid coatings, laminates, adhesives and in civil
engineering works. |
| Downloads |
TDS
(.pdf 27kb) |
|
| Grade |
TH7211 |
| Color1 |
2 |
| Viscosity2 |
35 - 80 |
| Amine value3 |
300 - 330 |
| Specific gravity4 |
0.95 |
| Equivalent
weight per active-H |
76 |
| Recommended
phr5 |
40 |
| Gel time6 |
80 - 120 |
| Thin film
set t ime7 |
9 - 12 |
| Tg8 |
40 - 5,013 |
| General Comments |
Low viscosity
and good colour makes it ideal for pot life enhancer
for other curing agents, high solids/solvent free
coatings, floorings, laminates and adhesives. Extremely
good carbonation resistance. |
| Downloads |
TDS
(.pdf 28kb) |
|
| Grade |
TH7212 |
| Color1 |
2 |
| Viscosity2 |
15 - 30 |
| Amine value3 |
690 - 720 |
| Specific gravity4 |
1.05 |
| Equivalent
weight per active-H |
48 |
| Recommended
phr5 |
25 |
| Gel
time6 |
30
- 50 |
| Thin film
set t ime7 |
2 - 4 |
| Tg8 |
min 40 |
| General Comments |
Very low viscosity
can be used at lower temperatures. It shows rapid
build-up of mechanical strength as well as good adhesion
to concrete. Can be used in adhesives, concrete impregnation
and patch repair compounds.Ideal for crack injection
systems. |
| Downloads |
TDS
(.pdf 28kb) |
|
| Grade |
TH7222 |
| Color1 |
8 |
| Viscosity2 |
800 - 1,500 |
| Amine value3 |
- |
| Specific gravity4 |
- |
| Equivalent
weight per active-H |
- |
| Recommended
phr5 |
- |
| Gel time6 |
20 - 40 |
| Thin film
set t ime7 |
2 - 5 |
| Tg8 |
- |
| General Comments |
A low viscosity
modified amine curing agent. It gives hard, glossy
surface when used with epoxy resin. Used in high solid/low
VOC solvent free coatings, adhesives and decorative
floorings. |
| Downloads |
TDS
(.pdf 26kb) |
|
| Grade |
TH7222N |
| Color1 |
8 |
| Viscosity2 |
450 - 700 |
| Amine value3 |
- |
| Specific gravity4 |
- |
| Equivalent
weight per active-H |
- |
| Recommended
phr5 |
- |
| Gel time6 |
20 - 35 |
| Thin film
set time7 |
3 - 5 |
| Tg8 |
- |
| General Comments |
A low viscosity
modified amine curing agent. It gives hard, glossy
surface when used with epoxy resin. Used in high solid/low
VOC solvent free coatings, adhesives and decorative
floorings. |
| Downloads |
TDS
(.pdf 28kb) |
|
| Grade |
TH7903 |
| Color1 |
8 |
| Viscosity2 |
1,200 - 1,800 |
| Amine value3 |
760 - 800 |
| Specific gravity4 |
1.08 |
| Equivalent
weight per active-H |
50 |
| Recommended
phr5 |
26 |
| Gel time6 |
14 - 18 |
| Thin film
set time7 |
2 - 3 |
| Tg8 |
50 - 5,014 |
| General Comments |
Faster cure
at lower temperatures and can be cured in presence
of high humid conditions. Mainly used in chemically
resistant coatings, adhesives, laminates, mortars,
gel coats, concrete repairing compounds and for bonding
old concrete to new concrete. |
| Downloads |
TDS
(.pdf 28kb) |
|
| Grade |
TH7905 |
| Color1 |
5 |
| Viscosity2 |
400 - 600 |
| Amine value3 |
350 - 390 |
| Specific gravity4 |
1 |
| Equivalent
weight per active-H |
75 |
| Recommended
phr5 |
40 |
| Gel time6 |
15 - 20 |
| Thin film
set t ime7 |
1 - 2 |
| Tg8 |
75 - 8,515 |
| General Comments |
High reactivity
and low viscosity. Excellent resistance to organic
acids and solvents. Good adhesion to concrete and
steel. Can be cured at low temperature and in presence
of high humidity. |